Abstract
The La2O3-doped basaltic glass simulated high-level waste form (HLW) was prepared by the solid-state melt method. The simulated waste La2O3 maximum loading and the doping effect on structure, thermal stability, leaching behavior, density, and hardness of basaltic glasses were studied. XRD and SEM results show that the simulated waste loading of La2O3 in basaltic glass can be up to ~46 wt.%, and apatite (CaLa4(SiO4)3O) precipitates when the content of La2O3 reaches 56 wt.%. Raman results indicate that the addition of La2O3 breaks the Si–O–Si bond of large-membered and four-membered, but the number of A13+ involved in the formation of the network increase. Low content of La2O3 can help to repair the glass network, but it destroys the network as above 26 wt.%. DSC results show the thermal stability of simulated waste forms first increases and then decreases with the increase of La2O3 content. With the increase of La2O3 content, the density of the simulated waste form increases, and the hardness decreases. The leaching chemical stability of samples was evaluated by the ASTM Product Consistency Test (PCT) Method, which show that all the samples have good chemical stability. The leaching rates of La and Fe are three orders of magnitude lower than those of the other elements. Among them, L36 has the best comprehensive leaching performance.
Funder
Major Science and Technology Special Project of Advanced, Materials in Sichuan Province, China
Subject
General Materials Science
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献