Structural and Optical Properties of Bi12NiO19 Sillenite Crystals: Application for the Removal of Basic Blue 41 from Wastewater

Abstract

This article covers the structural and optical property analysis of the sillenite Bi12NiO19 (BNO) in order to characterize a new catalyst that could be used for environmental applications. BNO crystals were produced by the combustion method using Polyvinylpyrrolidone as a combustion reagent. Different approaches were used to characterize the resulting catalyst. Starting with X-ray diffraction (XRD), the structure was refined from XRD data using the Rietveld method and then the structural form of this sillenite was illustrated for the first time. This catalyst has a space group of I23 with a lattice parameter of a = 10.24 Å. In addition, the special surface area (SSA) of BNO was determined by the Brunauer-Emmett-Teller (BET) method. It was found in the range between 14.56 and 20.56 cm2·g−1. Then, the morphology of the nanoparticles was visualized by Scanning Electron Microscope (SEM). For the optical properties of BNO, UV-VIS diffusion reflectance spectroscopy (DRS) was used, and a 2.1 eV optical bandgap was discovered. This sillenite′s narrow bandgap makes it an effective catalyst for environmental applications. The photocatalytic performance of the synthesized Bi12NiO19 was examined for the degradation of Basic blue 41. The degradation efficiency of BB41 achieved 98% within just 180 min at pH ~9 and with a catalyst dose of 1 g/L under visible irradiation. The relevant reaction mechanism and pathways were also proposed in this work.