Abstract
The application of carbon nanotubes to produce cementitious composites has been extensively researched. However, the dispersion of this nanomaterial remains a technical limitation for its use. Thus, initially, this study assessed the stability of carboxyl-functionalized CNT on aqueous suspensions and simulated cement pore solution for 6 h through UV–visible spectroscopy. Subsequently, a CNT content of 0.1% by cement weight was incorporated into the cement pastes, and the compressive strength after 7, 14, 28, and 91 days was evaluated. In addition, the porosity of the CNT cementitious composites at 28 days of hydration was investigated by mercury intrusion porosimetry (MIP), and the microstructure was evaluated via scanning electron microscopy (SEM). The simulated cement pore solution’s alkaline environment affects the CNT stability, progressively reducing the dispersed CNT concentration over time. CNT reduced the cementitious matrix pores < 50 nm by 8.5%; however, it resulted in an increase of 4.5% in pores > 50 nm. Thus, CNT incorporation did not significantly affect the compressive strength of cement pastes. SEM results also suggested a high porosity of CNT cementitious composites. The CNT agglomeration trend in an alkaline environment affected the CNT performance in cement-based nanocomposites.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献