Abstract
The aim of this work was to evaluate the porosity, microstructure, hardness, and electrochemical behavior of AISI 316 steel layers deposited on an AISI 347 steel substrate using the LMD process. Depositions of two, four, and six layers with a 0.5 mm height for each layer were performed at a speed of 375 mm/min, a power of 250 W, a focal distance of 5 mm, and without overlapping laser tracks. The results showed epitaxial growth of the deposited layers in relation to the substrate and a predominantly austenitic microstructure with ferrite as the substrate. The deposited layers presented a dendritic microstructure with a mean porosity of 4.5%. The porosity decreased as the number of deposited layers increased, affecting the pitting corrosion resistance. The sample with six deposited layers showed greater pitting corrosion resistance, whereas the corrosion current speeds were similar for the studied samples. Vickers hardness tests showed that the hardness decreased as the distance from the substrate increased, and the hardness decreased close to the remelted regions.
Funder
São Paulo Research Foundation
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior—Brasil
Subject
General Materials Science,Metals and Alloys
Reference38 articles.
1. Additive manufacturing of Ti–6Al–4V components by shaped metal deposition: Microstructure and mechanical properties;Baufeld;Mater. Des.,2010
2. Kranz, J., Herzog, D., and Emmelmann, C. (2015). Design guidelines for laser additive manufacturing of lightweight structures in TiAl6V4. J. Laser Appl., 27.
3. Remanufacturing of turbine blades by laser direct deposition with its energy and environmental impact analysis;Wilson;J. Clean. Prod.,2014
4. Characterization of stainless steel parts by Laser Metal Deposition Shaping;Zhang;Mater. Des.,2014
5. Volpato, N., Munhoz, A.L.J., Costa, C.A., Ahrens, C.H., de Carvalho, J., dos Santos, J.R.L., da Silva, J.V.L., Foggiatto, J.A., and Lima, M.S.F. (2017). Manufatura Aditiva–Tecnologias e Aplicações da Impressão 3D, Blucher. [1st ed.].
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献