The Effect of Annealing Treatment on the Microstructure and Texture of a Cold-Rolled TiNiFe Shape Memory Alloy Tube

Abstract

The effect of annealing treatment on the microstructure and texture of a Ti50Ni47Fe3 shape memory alloy tube was studied. The results show that the recrystallization process of a cold-rolled Ti50Ni47Fe3 alloy tube occurs at 600 °C. The microstructure changes from long striped grains to equiaxed recrystallized grains. The main texture of the alloy tube is the fiber texture <111> parallel to RD. With the increase in the annealing temperature, the crystal orientation of the alloy gradually turned to (111)<112>, and a series of secondary textures were distributed along the γ orientation line when the alloy was annealed at a lower temperature (450~600 °C). When the alloy was annealed at 650 °C, the growth of recrystallized grains made the grain orientation change, which led to the weakening of the γ-fiber texture and the formation of recrystallization textures.