Study of the Microstructure and Mechanical Property Relationships of Gas Metal Arc Welded Dissimilar Protection 600T, DP450 and S275JR Steel Joints

Abstract

The need for combining dissimilar materials is steadily increasing in the manufacturing industry, and the resulting products are expected to always have high performance. While there are various methods available for joining such material pairs, one of the commonly preferred techniques is fusion welding. In this study, three different steel materials (Protection 600T, DP450, and S275JR) were joined using gas metal arc welding (GMAW) in different combinations (similar/dissimilar). The microstructure and mechanical properties of the joints were evaluated. Tensile test, Vickers microhardness (HV 0.1), bending, Charpy V-notch impact testing, and microstructure examinations were conducted to analyze the weld and heat-affected zone. The tensile strengths of the base metal materials Protection 600T, DP450, and S275JR were found to be 1524.73 ± 18.7, 500.8 ± 10.4, and 508.5 ± 9.5 MPa, respectively. In welded samples of similar materials, the highest efficiency was found to be 103.05% for DP450/DP450, while in dissimilar welded joints, it was 105.5% for the DP450/S275JR pair. Hardness values for the base materials Protection 600T, DP450, and S275JR were measured as 526.5 ± 10.5, 153.8 ± 1.8, and 162.5 ± 5.2, respectively. In all welded samples, there was an increase in hardness in the weld zone (due to the welding wire) and the heat-affected zone (due to grain size refinement). While the impact energy values of similar material pairs were close to the base material impact energy values, the impact energy values of dissimilar material pairs varied according to the base materials. In addition, in joints made with similar materials, the bending force was close to the base materials, while a decrease in bending force was observed in joints formed with dissimilar materials. As a result, the welding of DP450 and S275JR materials was carried out efficiently. Protection 600T was welded with other materials, but its welding strength was limited to the strength of the material with low mechanical properties.