Effect of Interlaminar Toughness on the Residual Compressive Capacity of Carbon Fiber Laminates with Different Types of Delamination

Abstract

In this paper, the effect of interlaminar properties and the type of delamination defects on the residual compression properties of carbon fiber laminates were experimentally investigated. A new method, which employed magnetic force to guide the arrangement direction of stainless steel particles between layers of laminates, was adopted to improve the interlayer toughness. The digital image correlation, C-scan, and micro-CT were used to measure and identify the compression failure damages. Test results showed that the compressive strength of the intact carbon fiber laminates was 299.37 MPa, and the one of specimens containing the deeply buried delamination, the through-width delamination, and the surface delamination decreased by 55.98 MPa, 58.69 MPa, and 60.23 MPa, respectively. The compressive strength of the specimens containing the deeply buried delamination only decreased by 14.01 MPa when the mode I toughness increased by 81.88%, and the specimen containing the surface delamination only decreased by 30.86 MPa when the mode II fracture toughness increased by 87.72%. However, improving the fracture toughness could not strengthen the specimens containing the through-width delamination. Moreover, a qualitative dynamic damage relationship, which described the relationship between delamination expansion and compression damage vividly, was proposed. The reason the increase of the toughness could improve the residual compression performance of the laminates containing delamination was that the higher fracture toughness hindered the secondary expansion of the delamination during the compression process so that the delamination area could almost remain unchanged.