The oxygen reduction reaction (ORR) activity of a Cu-doped Ba0.5Sr0.5FeO3−δ (Ba0.5Sr0.5Fe1−xCuxO3−δ, BSFCux, x = 0, 0.05, 0.10, 0.15) perovskite cathode was investigated in terms of oxygen vacancy formation and valence band structure. The BSFCux (x = 0, 0.05, 0.10, 0.15) crystallized in a cubic perovskite structure (Pm3¯m). By thermogravimetric analysis and surface chemical analysis, it was confirmed that the concentration of oxygen vacancies in the lattice increased with Cu doping. The average oxidation state of B-site ions decreased from 3.583 (x = 0) to 3.210 (x = 0.15), and the valence band maximum shifted from −0.133 eV (x = 0) to −0.222 eV (x = 0.15). The electrical conductivity of BSFCux increased with temperature because of the thermally activated small polaron hopping mechanism showing a maximum value of 64.12 S cm−1 (x = 0.15) at 500 °C. The ASR value as an indicator of ORR activity decreased by 72.6% from 0.135 Ω cm2 (x = 0) to 0.037 Ω cm2 (x = 0.15) at 700 °C. The Cu doping increased oxygen vacancy concentration and electron concentration in the valence band to promote electron exchange with adsorbed oxygen, thereby improving ORR activity.
Funder
Pusan National University
Subject
General Materials Science
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献