The aim of this work was to prepare sugar alcohol-based deep eutectic solvents (DES) and test them as starch plasticizers. Thermoplastic starch (TPS) films were obtained via a simple and convenient thermocompression method. Influence of starch/DES premixtures conditioning (preheating, storage time) on TPS properties was investigated. TPS/sorbitol (S)-based DES exhibited similar tensile strength (TS) (8.6 MPa) but twice higher elongation at the break (ε) (33%) when compared with TPS plasticized only with S. Extra treatment, i.e., heating or prolonged storage time, facilitated starch/DES plasticizing. Starch with selected DES was also extruded and the influence of preconditioning and extrusion rotational speed were subsequently studied on thermocompressed films. Extrusion at 100 rpm led to films with TS up to ca. 10 MPa and ε up to 52%. Some differences in film samples morphology obtained via two processing methods were observed. X-ray diffractograms revealed that extruded samples exhibited a V-type peak at 18.2°, with intensity depending on plasticizer total molecular size. Applied techniques (mechanical tests, XRD, Dynamic Mechanical Analysis (DMA), FTIR-Attenuated Total Reflection (ATR), and moisture sorption) indicated that S-based DES forms stronger interactions with starch than glycerol (G) only used as conventional plasticizer, thus leading to better mechanical properties and inhibited tendency to starch recrystallization (studied up to one year).
Subject
Polymers and Plastics,General Chemistry
Reference48 articles.
1. Chapter 7-Starch thermal processing: Technologies at laboratory and semi-industrial scales;Xie,2017
2. Progress in starch modification in the last decade
3. Sorption of Cu2+ and Fe3+ onto starch grafted copolymers obtained via reactive extrusion;Schmidt;Przemysł Chem.,2010
4. Thermoplastic starches: Properties, challenges, and prospects
5. The effect of plasticizers on thermoplastic starch compositions obtained by melt processing
Cited by
27 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献