Abstract
The hot-drawing process of polyacrylonitrile (PAN) fibers is an important step during the production of PAN-based carbon fibers. In this study, supercritical carbon dioxide (Sc-CO2) was used as one kind of media for thermal stretching of PAN fibers to study the effect of different pressures of Sc-CO2 on crystallinity, degree of orientation and mechanical property of PAN fibers during the hot-drawing process. The changes of microstructure and mechanical properties in the PAN fibers were investigated by wide-angle X-ray diffraction, small angle X-ray scattering and monofilament strength analysis. The results showed that as the pressure increased, the crystallinity and degree of orientation of PAN fibers increased. Furthermore, when the pressure was 10 MPa, the crystallinity increased from 69.78% to 79.99%, which was the maximum crystallinity among the different pressures. However, when the pressure was further increased, the crystallinity and degree of orientation of the fibers were reduced. The test results of the mechanical properties were consistent with the trends of crystallinity and degree of orientation, showing that when the pressure was 10 MPa, the tensile strength of the fibers increased from 4.59 cN·dtex−1 to 7.06 cN·dtex−1 and the modulus increased from 101.54 cN·dtex−1 to 129.55 cN·dtex−1.
Subject
Polymers and Plastics,General Chemistry
Reference36 articles.
1. History and Structure of Carbon Fibers;Park,2018
2. Novel Carbon Fibers and Their Composites;Park,2018
3. Development and application of carbon fiber brush for DC motor;Zhi-Ping;Carbon,2017
4. Mechanical characterization of carbon fiber reinforced plastics specimens for aerospace applications
5. Preparation and characterization of polyacrylonitrile-based carbon fiber papers
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献