Evaluation of Stereolithography-Based Additive Manufacturing Technology for BaTiO3 Ceramics at 465 nm

Author:

Chugunov SvyatoslavORCID,Smirnov Andrey,Kholodkova Anastasia,Tikhonov Andrey,Dubinin OlegORCID,Shishkovsky IgorORCID

Abstract

A piezoceramic BaTiO3 material that is difficult for 3D printing was tested with a homemade laser-based stereolithography (SLA) setup. The high light absorbance of BaTiO3 in the spectral range of 350–410 nm makes this material hardly usable with most commercial SLA 3D printers. The typical polymerization depth of BaTiO3 ceramic pastes in this spectral range hardly reaches 30–50 µm for 40 vol % powder loading. A spectral change to 465 nm was realized in this work via a robot-based experimental SLA setup to improve the 3D printing efficiency. The ceramic paste was prepared from a preconditioned commercial BaTiO3 powder and used for 3D printing. The paste’s polymerization was investigated with variation of powder fraction (10–55 vol %), speed of a laser beam (1–10 mm/s, at constant laser power), and a hatching spacing (100–1000 µm). The polymerization depths of over 100 µm were routinely reached with the 465 nm SLA for pastes having 55 vol % powder loading. The spectral shift from 350–410 nm spectral region to 465 nm reduced the light absorption by BaTiO3 and remedied the photopolymerization process, emphasizing the importance of comprehensive optical analysis of prospective powders in SLA technology. Two multi-layered objects were 3D-printed to demonstrate the positive effect of the spectral shift.

Funder

Russian Science Foundation

Publisher

MDPI AG

Subject

Fluid Flow and Transfer Processes,Computer Science Applications,Process Chemistry and Technology,General Engineering,Instrumentation,General Materials Science

Cited by 6 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3