Push-Out Bond Strength Evaluation of Fiber-Reinforced Composite Resin Post Cemented with Self-Adhesive Resin Cement Using Different Adhesive Bonding Systems

Abstract

The purpose of this in vitro study was to evaluate the push-out bond strength of fiber-reinforced resin posts using self-adhesive cements with different adhesive systems. A total of 50 single-rooted human maxillary premolars with fully developed apices and 15–16 mm straight root canals were selected. The teeth were divided into 10 groups with coronal and apical parts according to the adhesive bonding system and luting material used: one universal adhesive with MDP-containing self-adhesive resin cement; another universal adhesive with MDP-containing self-adhesive resin cement; universal primer with MDP-containing self-adhesive resin cement; universal primer with dual-cure resin cement; MDP-containing self-adhesive resin cement only (Control). Each specimen was subjected to a fatigue load of 600,000 cycles using a chewing simulator with sliding movement and cut horizontally for push-out bond strength testing. Statistical evaluation consisted of a one-way ANOVA test using SPSS v23.0. The highest bond strength (7.05 MPa) was obtained in the coronal part of the Single Bond universal group treated with MDP-containing self-adhesive resin cement and the lowest strength (4.77 MPa) was observed in apical part of MDP-containing self-adhesive resin cement group (Control). However, the one-way ANOVA results showed no significant difference between all 10 groups (p > 0.05). The self-adhesive cement without adhesive bonding showed no statistically different value compared to self-adhesive cements with adhesive bonding.