Abstract
The preparation method and calcination temperature of metal-organic framework (MOFs)-derived materials are critical factors affecting catalytic performance. In this work, the preparation conditions of MOFS precursors were optimized, and zinc-based catalysts with different activities (MOF5-700, MOF5-750, and MOF5-800) were obtained by pyrolysis of MOFS precursors under nitrogen, which were then applied to an acetylene acetoxylation reaction system. According to the results, the conversion rate of acetic acid under catalysis was significantly different. (MOF5-700 (48%), MOF5-750 (62%), and MOF5-800 (22%)). Comparing the activity of the catalyst with the industrial catalyst Zn(OAc)2/AC (20%), MOF5-750 showed higher activity, and the acetic acid conversion rate remained around 60% after 50 h of stability testing. By characterization analysis, MOFs-derived materials were obtained after proper temperature pyrolysis. They have high mesoporous content, defects, and oxygen-containing functional groups and can maintain a good crystal structure, greatly reducing the loss of active components. This is the main reason for the good performance of the MOF5-750 catalyst in acetylene acetoxylation. Thus, the preparation conditions and favorable pyrolysis temperature of MOF derivative catalysts play a key role in the catalytic performance of acetylene acetoxylation.
Funder
Science and Technology Project of Xinjiang Bingtuan Supported by Central Government
National Natural Science Foundation of China
Xinjiang Uygur Autonomous Region Postgraduate Innovation Project
Subject
Physical and Theoretical Chemistry,Catalysis,General Environmental Science
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献