Mesoporous Cobalt Ferrite Nanosystems Obtained by Surfactant-Assisted Hydrothermal Method: Tuning Morpho-structural and Magnetic Properties via pH-Variation

Author:

Palade Petru,Comanescu CezarORCID,Kuncser Andrei,Berger DanielaORCID,Matei CristianORCID,Iacob NicusorORCID,Kuncser Victor

Abstract

A facile and cheap surfactant-assisted hydrothermal method was used to prepare mesoporous cobalt ferrite nanosystems with BET surface area up to 151 m2/g. These mesostructures with high BET surface areas and pore sizes are made from assemblies of nanoparticles (NPs) with average sizes between 7.8 and 9.6 nm depending on the initial pH conditions. The pH proved to be the key factor for controlling not only NP size, but also the phase purity and the porosity properties of the mesostructures. At pH values lower than 7, a parasite hematite phase begins to form. The sample obtained at pH = 7.3 has magnetization at saturation Ms = 38 emu/g at 300 K (54.3 emu/g at 10 K) and BET surface area SBET = 151 m2/g, whereas the one obtained at pH = 8.3 has Ms = 68 emu/g at 300 K (83.6 emu/g at 10 K) and SBET = 101 m2/g. The magnetic coercive field values at 10 K are high at up to 12,780 Oe, with a maximum coercive field reached for the sample obtained at pH = 8.3. Decreased magnetic performances are obtained at pH values higher than 9. The iron occupancies of the tetrahedral and octahedral sites belonging to the cobalt ferrite spinel structure were extracted through decomposition of the Mössbauer patterns in spectral components. The magnetic anisotropy constants of the investigated NPs were estimated from the temperature dependence of the hyperfine magnetic field. Taking into consideration the high values of BET surface area and the magnetic anisotropy constants as well as the significant magnetizations for saturation at ambient temperature, and the fact that all parameters can be adjusted through the initial pH conditions, these materials are very promising as recyclable anti-polluting agents, magnetically separable catalysts, and targeted drug delivery vehicles.

Publisher

MDPI AG

Subject

General Materials Science,General Chemical Engineering

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3