Slag Modification in Reduction of Kiviniemi Ferrous Scandium Concentrates

Abstract

Several research projects are currently focused on the search for new sources of scandium due to its expected increasing demand in advanced technology applications. The Kiviniemi Fe-Sc-enriched mafic intrusion is a potential primary source for Sc. According to the recent investigations on the FeO component reduction in the Kiviniemi magnetic Sc concentrate at various end temperatures, complete FeO reduction is achieved at the highest experimental temperature (1500 °C). However, efficient separation of metal from the Sc2O3-enriched slag is hindered by the high viscosity of the slag. In this study, investigations of the Kiviniemi-type concentrate reduction characteristics are complemented from three perspectives: (1) slag modification with CaF2 and/or CaO to promote the reduction of the FeO component and metal separation, (2) reduction characteristics of the concentrates with a slightly different modal mineralogy and chemical composition, and (3) description of the main features of the progression of reduction at selected temperatures (950, 1050, 1150, 1250, and 1350 °C) with CaO addition. Both CaF2 and CaO increase conversion rates at a lower temperature region and promote the separation of metal from the slag. High-temperature behavior of the concentrates used in this study is essentially similar, although the main reduction stage is initiated at a slightly higher temperature for concentrates with less amphibole and a higher amount of nonferrous gangue minerals. Only after the complete decomposition and melting of clinopyroxene and nonferrous minerals of the concentrate, the final reduction of the FeO component from the slag can take place.