Nanocurcumin Release from Self-Cured Acrylic Resins; Effects on Antimicrobial Action and Flexural Strength

Author:

Soleymanijadidi Parsa1,Moradi Meysam1,Hamedirad Fahimeh1,Ghanavati Zahra1,Maleki Dizaj Solmaz23ORCID,Salatin Sara4

Affiliation:

1. Dental Materials Research Center, Health Research Institute, Babol University of Medical Sciences, Babol 47176-4774, Iran

2. Dental and Periodontal Research Center, Tabriz University of Medical Sciences, Tabriz 51548-53431, Iran

3. Department of Dental Biomaterials, Faculty of Dentistry, Tabriz University of Medical Sciences, Tabriz 51548-53431, Iran

4. Neurosciences Research Center, Tabriz University of Medical Sciences, Tabriz 51548-53431, Iran

Abstract

The placement of orthodontic appliances into the oral area can lead to infection, inflammatory and gingival collapse. Using an antimicrobial and anti-inflammatory material in the matrix of orthodontic appliance may help to reduce these issues. This study aimed to assess the release pattern, the antimicrobial action and the flexural strength of self-cured acrylic resins after adding different weight percentages of curcumin nanoparticles (nanocurcumin). In this in-vitro study, 60 acrylic resin samples were divided into five groups (n = 12) based on the weight percentage of curcumin nanoparticles added to the acrylic powder (0 for control, 0.5, 1, 2.5, and 5%). Then, the dissolution apparatus was used for the release assessment of nanocurcumin form the resins. For antimicrobial action assessment, the disk diffusion method was used and a three-point bending test was performed with a speed of 5 mm/min to determine the flexural strength. Data were analyzed using one-way analysis of variance (ANOVA) and Post-Hoc Tukey tests (with p < 0.05 as significant level). The microscopic images showed the homogeny distribution of nanocuricumin in self-cured acrylic resins in varied concentrations. The release pattern showed a two-step release pattern for all concentrations of nanocurcumin. The one-way ANOVA outcomes indicated that adding curcumin nanoparticles to self-cured resin increased the diameter of the inhibition zones for the groups against Streptococcus mutans (S. mutans) significantly (p < 0.0001). Additionally, as the weight percentage of curcumin nanoparticles increased, the flexural strength decreased (p < 0.0001). However, all strength values were higher than the standard value (50 MPa). No significant difference was detected between the control group and the group with 0.5 percent (p = 0.57). Considering the proper release pattern and the potent antimicrobial activity of curcumin nanoparticles, then the preparing self-cured resins containing curcumin nanoparticles can be beneficial for antimicrobial aims without damaging the flexural strength to use in orthodontic removable applications.

Funder

The Vice-Chancellor for Research at Babol University of Medical Sciences, Babol, Iran

Publisher

MDPI AG

Subject

Bioengineering

Cited by 3 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3