Highly Active Ag-Cu Nanocrystal Catalyst-Coated Brewer’s Spent Grain Biochar for the Mineralization of Methyl Orange and Methylene Blue Dye Mixture

Abstract

The aim of the present work is to valorise the brewing industry’s waste, i.e., brewer’s spent grain (BSG), into functional biocarbon for environmental catalysis applications. In this context, cost-effective and environmentally friendly biochar support coated with in-situ-generated Ag-Cu nanocrystals, was developed via the wet impregnation of BSG biomass powder with copper (II) nitrate trihydrate and silver nitrate aqueous solution prior to pyrolysis at moderate temperature (500 °C). Small-size homogenously distributed Ag-Cu nanocrystals (≤80 nm) on the surface of the biochar (Biochar@Ag-Cu) were observed by field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). Elemental compositions were determined by X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray analysis (EDX). The crystalline nature of the nanoparticles was confirmed by X-ray powder diffraction (XRD). Information about the thermal stability of the materials and quality were obtained by thermogravimetric analysis (TGA) and Raman, respectively. The potentiality of the Biochar@Ag-Cu catalyst in the field of pollutant removal is demonstrated by taking methyl orange and methylene blue as model dyes. A kinetics study was performed and analyzed by UV–vis spectroscopy. Its highly active catalytic nature is proved by the complete mineralization of the methyl orange dye (100%) through oxidative degradation. The reusability of the catalyst has shown 96% removal efficiency after 3 cycles. The linear plot of −Ln (CA/C0) vs. time (R2 = 0.9892) reveals that the mineralization of the methyl orange dye follows pseudo-first-order kinetics (k = 0.603 × 10−2 min−1). A methyl orange + methylene blue dye mixture degradation study has revealed the faster kinetics of the present catalyst towards methylene blue degradation. The current study suggests that BSG Biochar@Ag-Cu can be a potential candidate in contribution towards SDG 6.