Author:
Garbev Krassimir,Ullrich Angela,Beuchle Günter,Bergfeldt Britta,Stemmermann Peter
Abstract
The synthesis of low-temperature belite (C2S) clinker from wastes of autoclaved aerated concrete and limestone was studied in the presence of CaCl2 as a mineralizing agent. Synthetic chlorellestadite (SCE; Ca10(SiO4)3(SO4)3Cl2) forms in experiments at temperatures between 700 and 1200 °C. Samples were investigated by X-ray diffraction and Raman spectroscopy. In general, the amount of SCE depends mainly on the sulfate content and to a lesser extent on the synthesis temperature. At lower temperatures of formation, a non-stoichiometric SCE seems to crystallize in a monoclinic symmetry similar to hydroxylellestadite. Rietveld refinements revealed the presence of chlorine and calcium vacancies. Raman spectroscopy proved the partial substitution of sulfate by CO32− groups in ellestadites formed at 800 °C and 900 °C in air. Incorporation of CO3 results in a shorter unit cell parameters and smaller cell volume similar to CO3−apatite. At low temperatures, SCE coexists with spurrite intermixed on a very fine nm scale. At temperatures above 900 °C in air, ellestadite is carbonate-free and above 1000 °C chlorine loss starts in all samples.
Funder
Federal Ministry of Education and Research
Subject
Geology,Geotechnical Engineering and Engineering Geology
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献