Abstract
Fatigue damage accumulation will not only cause the degradation of material performance but also lead to the growth of effective stress and critical stiffness. However, the existing fatigue reliability models usually ignore the effective stress growth and its influence on the critical stiffness of a composite material. This study considers the combined effects of performance degradation and effective stress growth, and a pair of fatigue reliability models for a composite material are presented. Firstly, the fatigue damage in a composite material is quantified by its performance degradation, and the fitting accuracy of several typical fatigue damage models is compared. Subsequently, the uncertainties of initial strength and initial stiffness are considered, and a pair of probabilistic models of residual strength and residual stiffness are proposed. The performance degradation data of Gr/PEEK [0/45/90/−45]2S laminates are utilized to verify the proposed probabilistic models. Finally, the effective stress growth mechanism and its influence on the failure threshold are elaborated, and a pair of fatigue reliability models for composite materials are developed. Moreover, the differences between the strength-based and stiffness-based reliability analysis results of composite materials are compared and discussed.
Funder
National Natural Science Foundation of China
Fundamental Research Funds for Universities in Xinjiang Uygur Autonomous Region
Natural Science Foundation of Xinjiang Uygur Autonomous Region
Key Research and Development Program of Xinjiang Uygur Autonomous Region
Reference51 articles.
1. Usage of additive manufacturing and topology optimization process for weight reduction studies in the aviation industry;Sarayakupolu;Adv. Sci. Technol. Eng. Syst. J.,2021
2. Parveez, B., Kittur, M.I., Badruddin, I.A., Kamangar, S., Hussien, M., and Umarfarooq, M.A. (2022). Scientific advancements in composite materials for aircraft applications: A review. Polymers, 14.
3. Successes and challenges in non-destructive testing of aircraft composite structures;Towsyfyan;Chin. J. Aeronaut.,2020
4. Probabilistic framework for fatigue life assessment of notched components under size effects;Liao;Int. J. Mech. Sci.,2020
5. Assessment of failure rates and reliability of floating offshore wind turbines;Li;Reliab. Eng. Syst. Saf.,2022
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献