Liquid Nitrogen Flow Boiling Critical Heat Flux in Additively Manufactured Cooling Channels

Abstract

This paper presents an experimental characterization of liquid nitrogen (LN2) flow boiling in additively manufactured minichannels. There is a pressing need of concerted efforts from the space exploration and thermal transport communities to design high-performance rocket engine cooling channels. A close observation of the literature gaps warrants a systematic cryogenic flow boiling characterization of asymmetrically heated small (<3 mm) non-circular channels fabricated with advanced manufacturing technologies at mass flux > 3000 kg/m2s and pressure > 1 MPa. As such, this work presents the LN2 flow boiling results for three asymmetrically heated additively manufactured GR-Cop42 channels of 1.8 mm, 2.3 mm, and 2.5 mm hydraulic diameters. Twenty different tests have been performed at mass flux~3805–14,295 kg/m2s, pressures~1.38 and 1.59 MPa, and subcooling~0 and 5 K. A maximum departure from nucleate boiling (DNB)-type critical heat flux (CHF) of 768 kW/m2 has been achieved for the 1.8 mm channel. The experimental results show that CHF increases with increasing LN2 flow rate (337–459 kW/m2 at 25–57 cm3/s for 2.3 mm channel) and decreasing channel size (307–768 kW/m2 for 2.5–1.8 mm channel). Finally, an experimental DNB correlation has been developed with 10.68% mean absolute error.