Fatigue Crack Propagation Study of Bridge Steel Q345qD Based on XFEM Considering the Influence of the Stress Ratio

Abstract

In the past, fatigue cracks have appeared in the orthotropic steel decks of bridges shortly after they opened to traffic. Previous studies have shown that high tensile welding residual stress exists in welded joints of steel bridges, which significantly changes the average stress and stress ratio of the joints. However, traditional fatigue crack propagation (FCP) calculations based on the Paris equation do not consider the influence of the stress ratio. Steel Q345qD is a common material used in bridges. Therefore, it is meaningful to study the influence of the stress ratio on the FCP life of steel Q345qD. In this paper, an FCP equation based on the energy release rate considering the influence of the stress ratio is first derived and named the da/dN-ΔG-R equation. Next, three material parameters in the equation are determined based on the results from tests of steel Q345qD under different stress ratios. Then, a user subroutine based on the extended finite element method (XFEM) that considers the influence of the stress ratio is defined and the effects of mesh size are analyzed. Finally, the effects of the stress ratio on FCP are discussed and the adaptability of the da/dN-ΔG-R equation is verified by comparing the values obtained from the equation with experimental results. The results show that: with a 95% guarantee rate, three material parameters in the da/dN-ΔG-R equation are: log(C) = −10.71, m = 2.780, and γ = 0.957; in the numerical simulation, a mesh size of 1 mm is more appropriate than other mesh sizes as it shows better accuracy and efficiency; under the same energy release rate range, the crack growth rate decreases as the stress ratio increases; under the same loading amplitude and cycles, the fatigue life decreases as the stress ratio increases; and finally, the numerical results considering the influence of stress ratio based on the da/dN-ΔG-R equation are close to the test results, while the results without considering the stress ratio based on the Paris equation are inaccurate.