Hot compression tests were conducted to explore the deformation behavior of an extruded 7075 aluminum alloy bar at elevated temperatures. Specimens with 0°, 45°, and 90° angles along the extrusion direction were prepared. The compression temperatures were 300 and 400 °C, and the strain rates ranged from 0.001 to 0.1 s−1. The corresponding microstructures were characterized via OM and TEM, and the macroscopic texture was tested using XRD. The results indicated that the strength of the 7075 alloy decreases with higher compression temperatures and is in a proportional relationship with respect to the strain rate. During high-temperature compression, it is easier to stimulate atomic diffusion in the matrix, which can improve thermal activation abilities and facilitate dynamic recovery and dynamic recrystallization. In addition, the coarsening of precipitates also contributed to dynamic softening. When compressed at 300 °C, the stress levels of the 0° specimens ranked first, and those for the 45° specimens were the lowest. When compressed at 400 °C, the flow stresses of the specimens along three directions were comparable. The anisotropic mechanical behavior can be explained by the fiber grains and brass {011} <211> texture component. However, higher temperature deformation leads to recrystallization, which can weaken the anisotropy of mechanical properties.
Funder
National Natural Science Foundation of China
Scientific Research Fund of Hunan Provincial Education Department of China
Higher Educational Institutions of Hunan Province
Reference40 articles.
1. Berlanga-Labari, C., Biezma-Moraleda, M.V., and Rivero, P.J. (2020). Corrosion of cast aluminum alloys. Metals, 10.
2. Noga, P., Skrzekut, T., Wędrychowicz, M., Węglowski, M.S., and Węglowska, A. (2023). Research of friction stir welding (FSW) and electron beam welding (EBW) process for 6082-T6 aluminum alloy. Materials, 16.
3. Bhatta, L., Pesin, A., Zhilyaev, A.P., Tandon, P., Kong, C., and Yu, H. (2020). Recent development of superplasticity in aluminum alloys. Metals, 10.
4. Improving mechanical properties of AlSi10Mg aluminum alloy using ultrasonic melt treatment combined with T6 heat treatment;Vatansever;Kov. Mater.,2019
5. Development of a new approach to resistance spot weld AW-7075 aluminum alloys for structural applications: An experimental study–Part 1;Bamberg;J. Mater. Res. Technol.,2021
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献