Abstract
In this work, the effect of the substrate, Al 7075 alloy and 1H18NT9 stainless steel, on the microstructure and tribological properties of cold sprayed (Cr3C2-25(Ni20Cr))-(Ni-graphite) coatings was investigated. Both coatings were dense and did not reveal any discontinuities at the interfaces. They had similar Cr3C2 and graphite contents. Their microstructures showed a variety of grain sizes of the matrix phase between the inner part of the splat, showing large ones, and their boundaries, where elongated and nanostructured grains were formed during the deposition process. The coating deposited on the steel substrate revealed a slightly higher hardness and lower abrasive wear with the Al2O3 loose abrasive particles. The force required to destroy the durability of the coating–steel substrate system in the three-point bending test was higher than those of the other ones. The cermet deposit cold sprayed on steel and examined at 25 °C under 10 N revealed the best wear resistance and the lowest friction coefficient.
Subject
General Materials Science
Reference39 articles.
1. Cold Spray Technology;Papyrin,2007
2. Fundamentals and Applications;Champagne,2007
3. The Science and Engineering of Thermal Spray Coatings;Pawłowski,2008
4. Thermal Spray Fundamentals;Fauchais,2014
5. Engineering HVOF-Sprayed Cr3C2-NiCr Coatings: The Effect of Particle Morphology and Spraying Parameters on the Microstructure, Properties, and High Temperature Wear Performance
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献