The hydrogen storage properties of a multi-component alloy of composition Ti0.3V0.3Mn0.2Fe0.1Ni0.1 were investigated. The alloy was synthesized by arc melting and mechanical alloying, resulting in different microstructures. It was found that the as-cast alloy is multiphase, with a main C14 Laves phase matrix along with a BCC phase and a small amount of Ti2Fe-type phase. The maximum hydrogen storage capacity of the alloy was 1.6 wt.%. We found that the air-exposed samples had the same capacity as the as-cast sample but with a longer incubation time. Synthesis by mechanical alloying for five hours resulted in an alloy with only BCC structure. The hydrogen capacity of the milled alloy was 1.2 wt.%, lower than the as-cast one. The effect of ball milling of the as-cast alloy was also studied. Ball milling for five hours produced a BCC structure similar to the one obtained by milling the raw materials for the same time.
Funder
Natural Sciences and Engineering Research Council of Canada
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献