Abstract
Primary dendrite arm spacing (PDAS) is a crucial microstructural feature in nickel-based superalloys produced by laser cladding. In order to investigate the effects of process parameters on PDAS, a multi-scale model that integrates a 3D transient heat and mass transfer model with a quantitative phase-field model was proposed to simulate the dendritic growth behavior in the molten pool for laser cladding Inconel 718. The values of temperature gradient (G) and solidification rate (R) at the S/L interface of the molten pool under different process conditions were obtained by multi-scale simulation and used as input for the quantitative phase field model. The influence of process parameters on microstructure morphology in the deposition layer was analyzed. The result shows that the dendrite morphology is in good agreement with the experimental result under varying laser power (P) and scanning velocity (V). PDAS was found to be more sensitive to changes in laser scanning velocity, and as the scanning velocity decreased from 12 mm/s to 4 mm/s, the PDAS increased by 197% when the laser power was 1500 W. Furthermore, smaller PDAS can be achieved by combining higher scanning velocity with lower laser power.
Funder
National Key Research and Development Program of China
National Science and Technology Major Project
State Ministry of Science and Technology Innovation Fund of China
Subject
General Materials Science
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献