Abstract
Transparent fluorotellurite glasses were prepared by melt-quenching in the ternary system TeO2-Nb2O5-PbF2. The synthesis conditions were adjusted to minimize fluorine loss monitored as HF release. It was found that 10 mol% of Nb2O5 is the optimum content for PbF2 incorporation up to 35 mol% in the tellurite matrix without loss of glass forming ability. Such glass compositions exhibit a wide optical window from 380 nm to about 6 μm. Crystallization properties were carefully investigated by thermal analysis and compositions with higher PbF2 contents exhibit preferential precipitation of lead oxyfluoride Pb2OF2 at lower temperatures. The lead oxyfluoride crystallization mechanism is also governed by a volume nucleation, barely reported in tellurite glasses. Eu3+ doping of these glass compositions also promotes a more efficient nucleation step under suitable heat-treatments, resulting in transparent Eu3+-doped glass-ceramics whereas undoped glass-ceramics are translucent. Finally, Eu3+ spectroscopy pointed out a progressive, more symmetric surrounding around the rare earth ions with increasing PbF2 contents as well as higher quantum efficiencies. These new fluorotellurite glass compositions are promising as luminescent hosts working in the middle infrared.
Funder
Fundação de Amparo à Pesquisa do Estado de Minas Gerais
Conselho Nacional de Desenvolvimento Científico e Tecnológico
Agence Nationale de la Recherche
Subject
General Materials Science
Cited by
12 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献