Effects of Cr Doping and Water Content on the Crystal Structure Transitions of Ba2In2O5

Abstract

Temperature-dependent crystal structure alterations in the brownmillerite-type material Ba2In2O5 play a fundamental role in its applications: (i) photocatalytic CO2 conversion; (ii) oxygen transport membranes; and (iii) proton conduction. This is connected to a reversible uptake of up an equimolar amount of water. In this study, in situ X-ray and neutron diffraction were combined with Raman spectroscopy and solid-state nuclear magnetic resonance experiments to unravel the effects of Cr doping and water content on the crystal structure transitions of Ba2In2O5(H2O)x over a wide temperature range (10 K ≤ T ≤ 1573 K, x < 1). A mixture of isolated and correlated protons was identified, leading to a highly dynamic situation for the protons. Hence, localisation of the protons by diffraction techniques was not possible. Cr doping led to an overall higher degree of disorder and stabilisation of the tetragonal polymorph, even at 10 K. In contrast, a further disordering at high temperatures, leading to a cubic polymorph, was found at 1123 K. Cr doping in Ba2In2O5 resulted in severe structural changes and provides a powerful way to adjust its physical properties to the respective application.