Improved Oxidation and Hot Corrosion Resistance of 1Cr11Ni2W2MoV Stainless Steel at 650 °C by a Novel Glass-Ceramic Coating

Abstract

A novel glass-ceramic coating was applied onto the 1Cr11Ni2W2MoV stainless steel. The oxidation and corrosion behaviors of coated and uncoated steels were comparatively investigated in air and in the presence of NaCl + Na2SO4 eutectic deposits at 650 °C, respectively. Protective scales formed on the surface of stainless steel prevented the severe oxidation of the alloy. Catastrophic hot corrosion occurred on the steel when a salt film was attached, producing loose iron oxide layers and internal corrosion zone. The glass-ceramic coating acted as a barrier that effectively hindered the invasion of corrosive species during the oxidation and hot corrosion tests.