A Simple and Efficient Method for Preparing High-Purity α-CaSO4·0.5H2O Whiskers with Phosphogypsum

Author:

Lin Yan,Sun Hongjuan,Peng Tongjiang,Ding Wenjin,Li Xiang,Xiao Sha

Abstract

A simple and efficient approach for the high-purity CaSO4·2H2O (DH) whiskers and α-CaSO4·0.5H2O (α-HH) whiskers derived from such phosphogypsum (PG) was proposed. The impact of different experimental parameters on supersaturated dissolution–recrystallization and preparation processes of α-CaSO4·0.5H2O was elaborated. At 3.5 mol/L HCl concentration, the dissolution temperature and time were 90 °C and 20 min, respectively. After eight cycles and 5–8 times cycles, total crystallization amount of CaSO4·2H2O was 21.75 and 9.97 g/100 mL, respectively, from supersaturated HCl solution. The number of cycles affected the shape and amount of the crystal. Higher HCl concentration facilitated CaSO4·2H2O dissolution and created a much higher supersaturation, which acted as a larger driving force for phase transformation of CaSO4·2H2O to α-CaSO4·0.5H2O. The HCl solution system’s optimum experimental conditions for HH whiskers preparation involved acid leaching of CaSO4·2H2O sample, with HCl concentration 6.0 mol/L, reaction temperature 80 °C, and reaction time 30 min–60 min. Under the third cycle conditions, α-CaSO4·0.5H2O whiskers were uniform in size, clear, and distinct in edges and angles. The length range of α-CaSO4·0.5H2O whiskers was from 106 μm to 231 μm and diameter range from 0.43 μm to 1.35 μm, while the longest diameter ratio was 231. Purity of α-CaSO4·0.5H2O whiskers was approximately 100%, where whiteness reached 98.6%. The reuse of the solution enables the process to discharge no waste liquid. It provides a new reference direction for green production technology of phosphogypsum.

Funder

the National Key Research and Development Program

Publisher

MDPI AG

Subject

General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3