Facile Synthesis of Fluorinated Polysilazanes and Their Durable Icephobicity on Rough Al Surfaces

Abstract

Superhydrophobic Al surfaces with excellent durability and anti-icing properties were fabricated by coating dual-scale rough Al substrates with fluorinated polysilazane (FPSZ). Flat Al plates were etched using an acidic solution, followed by immersion in boiling water to generate hierarchical micro-nano structures on their surfaces. The FPSZ coatings were synthesized by grafting 1H,1H,2H,2H-perfluorodecyltrimethoxysilane (FAS-17), a fluoroalkyl silane), onto methylpolysilazane, an organopolysilazane (OPSZ) backbone. The high water contact angle (175°) and low sliding angle (1.6°) of the FPSZ-coated sample with an FAS-17 content of 17.3 wt% promoted the efficient removal of a frozen ice column with a low ice adhesion strength of 78 kPa at −20.0 °C (70% relative humidity), which was 4.3 times smaller than that of an OPSZ-coated surface. The FPSZ-coated Al surface suppressed ice nucleation, leading to a decrease in ice nucleation temperature from −19.5 to −21.9 °C and a delay in freezing time from 334 to 4914 s at −19.0 °C compared with the OPSZ-coated Al surface. Moreover, after 40 icing–melting cycles the freezing temperature of a water droplet on the FPSZ-coated Al surface remained unchanged, whereas that on the FAS-17-coated Al surface increased from −22.3 to −20.7 °C. Therefore, the durability of the polymeric FPSZ coating was superior to that of the FAS-17 monolayer coating.