Industrial Implementation of Aluminum Trihydrate-Fiber Composition for Fire Resistance and Mechanical Properties in Glass-Fiber-Reinforced Polymer Roofs

Author:

Zainudin Mohammad,Diharjo Kuncoro,Kaavessina Mujtahid,Setyanto DjokoORCID,Ubaidillah UbaidillahORCID

Abstract

It is difficult to obtain suitable fire resistance and mechanical properties for glass-fiber-reinforced polymer (GFRP) roof material in industrial applications. Although some efforts to improve the fire resistance properties of GFRP have been carried out, in practice this sometimes degrades the mechanical properties. Therefore, the base materials, such as filler and reinforcing fiber, must be appropriately combined to simultaneously improve both fire resistance and mechanical properties. The present study examines improvements in GFRP roof material by investigating the effect of aluminium trihydrate (ATH) as a filler and the combination of a chopped strand mat (CSM) with woven roving (WR) and stitched mat (STM) fibers as the reinforcement in a composite GFRP roof structure. The roof samples were prepared following industrial machine standards using the specified materials. The mechanical properties of GFRP were evaluated using tensile, flexural and impact tests, following ASTM D638, ASTM D790 and ASTM D256 standards, respectively. The fire properties were examined through fire tests following the ASTM D635 standard. The results show that the GFRP roof composed of CSM/WR fibers had a 40% higher tensile strength (103.5 MPa) compared with the GFRP roof without CSM fibers (73.8 MPa). The flexural strength of the GFRP roof with CSM/WR fibers was also 57% higher than the roof without fibers, with a ratio of 315.61 MPa to 201 MPa. With the use of CSM/WR fibers, the fire resistance also increased by 23%, resulting in a ratio of 4.31 mm/min to 5.32 mm/min. These results demonstrate that the combination of CSM/WR fibers as a reinforcement would be an excellent option for producing an improved GFRP roof with better industrial properties, especially when producing improved GFRP roofs using a continuous lamination machine.

Funder

Sebelas Maret University

Publisher

MDPI AG

Subject

Polymers and Plastics,General Chemistry

Reference42 articles.

1. Degradation of Glass Fiber Reinforced Polymer (GFRP) Material Exposed to Tropical Atmospheric Condition

2. The properties degradation of exposed GFRP roof

3. Flammability and Thermal Stability of Unsaturated Polyester Resin-Based Blends and Composites;Kandola,2019

4. Towards Selection Charts for Epoxy Resin, Unsaturated Polyester Resin and Their Fibre-Fabric Composites with Flame Retardants

5. ATH AS a filler of vinylester RESIN;Deswan;Int. J. Mech. Prod. Eng. Res. Dev.,2020

Cited by 4 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3