Fracture Resistance in Non-Vital Teeth: Absence of Interproximal Ferrule and Influence of Preparation Depth in CAD/CAM Endocrown Overlays—An In Vitro Study

Abstract

There is ample evidence to support the use of endocrowns to restore endodontic teeth. However, the influence of the position of the interproximal margins on fracture strength has not yet been studied. The aim was to determine the relationship between the apicocoronal position of the interproximal restorative margins and fracture resistance in nonvital teeth restored with CAD/CAM endocrown overlays. Forty extracted human maxillary premolars were prepared for endocrown overlay restorations without ferrule on the interproximal aspects and classified according to the position of the interproximal restoration margins in relation to the alveolar crest: 2 mm (group A), 1 mm (group B), 0.5 mm (group C), and 0 mm (group D). Fracture strength was measured using a universal testing machine applying a compressive force to the longitudinal tooth axis. Group A had a mean fracture resistance of 859.61 (±267.951) N, group B 1053.9 (±333.985) N, group C 1124.6 (±291.172) N, and group D 780.67 (±183.269) N, with statistical differences between groups. Group C had the highest values for fracture strength compared to the other groups (p < 0.05). The location of the interproximal margins appears to influence the fracture resistance of CAD/CAM endocrown overlays. A distance of 0.5 mm between the interproximal margin and the alveolar crest was associated with increased fracture resistance.