Abstract
The influence of the thermo-oxidative aging semi-crystalline polyethylene terephthalate process on the thermal and mechanical properties was analysed in the article. For this purpose, PET was aged at 140 °C for 21, 35 and 56 days. The research showed that as a result of aging, the amount of the crystalline phase increases by about 8%, which translates into the properties of the aged material. The glass transition and melt temperature of lamellar crystals formed during first and second crystallisation increase with aging. The mechanical properties of the material were analysed in the temperature range of 25 to 75 °C. The tests were showing an increase in Young’s modulus and a decrease in elongation at the break as a result of aging. This phenomenon was particularly visible during tests at 75 °C and during the morphological observation of the fracture surface, where the fracture character of the material changes from ductile to brittle. In the case of the material aged for the longest time, the temperature has a negligible influence on the elongation at break.
Funder
Department of Mechanics and Special Purpose, Military University of Technology
Subject
General Materials Science
Reference50 articles.
1. PET Production Volumehttps://www.businesswire.com/news/home/20170914005775/en/Global-Polyethylene-Terephtalate-Market-Report-2017---By-End-Use-Industries-Products-Regions---Research-and-Markets
2. The thermal degradation of PET and analogous polyesters measured by thermal analysis–Fourier transform infrared spectroscopy
3. Ageing of poly(ethylene terephthalate) and poly(ethylene naphthalate) un-der moderately accelerated conditions;Turnbull;J. Appl. Polym. Sci.,2012
4. Hydrolytic and thermal degradation of PET fibers and PET granule: The effects of crystallization, temperature, and humidity
5. Effect of aging of PET fibre on the mechanical properties of PET fibre reinforced cement composite;Machoviè;Ceram. Silikaty,2008
Cited by
40 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献