Microstructure and Key Properties of Phosphogypsum-Red Mud-Slag Composite Cementitious Materials

Author:

Ma Feiyue,Chen Liangliang,Lin Zhiwei,Liu Zhuo,Zhang Weichuan,Guo RongxinORCID

Abstract

Due to the low content of silicon and aluminum in red mud and the low reaction activity of red mud, when it was used to prepare composite cementitious materials, it was necessary to assist other aluminosilicates and improve their activity by certain methods. In this study, it was proposed to add slag to increase the percentage of silicon and aluminum in the system, and to improve the reactivity of the system through the activation effect of sulfate in phosphogypsum. The effects of slag and phosphogypsum contents on the mechanical properties and microstructures of composite cementitious materials were studied. X-ray diffraction analysis (XRD), thermogravimetric analysis (TG-DTG), and scanning electron microscopy (SEM) were used to analyze the effects of slag and phosphogypsum contents on the hydration products, microstructure, and strength formation mechanism of composite cementitious materials. The results show that with the increase of slag, the strength of the composite cementitious material increases gradually. When the slag content is 50%, the 28-day compressive strength reaches a maximum of about 14 MPa. Compared with the composite material without phosphogypsum, the composite cementitious material with 10–20% phosphogypsum showed higher strength properties, in which the 28-day compressive strength exceeds 24 MPa. The main reason for this is that the sulfate in phosphogypsum can cause the composite cementitious material to generate a large amount of ettringite and accelerate the dissolution of red mud and slag, increasing the release of aluminates, silicates, and Ca2+ to form more C-(A)-S-H and ettringite. In addition, a large amount of C-(A)-S-H makes ettringite and unreacted particles combine into a uniform and compact structure, thus improving the strength. When the content of phosphogypsum exceeds 40%, the 28-day compressive strength of the composite cementitious material drops below 12 MPa due to the presence of fewer hydration products and the expansion of ettringite.

Funder

Projects of Science and Technology Department of Yunnan Province

Publisher

MDPI AG

Subject

General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3