Electrical and Mechanical Properties of Sugarcane Bagasse Pyrolyzed Biochar Reinforced Polyvinyl Alcohol Biocomposite Films

Abstract

Biochar obtained from the oxygen-deficient thermochemical processing of organic wastes is considered to be an effective reinforcing agent in biocomposite development. In the present research, biocomposite film was prepared using sugarcane bagasse pyrolyzed biochar and polyvinyl alcohol (PVA), and its electrical and mechanical properties were assessed. The biocomposite films were produced by varying content (5 wt.%, 8 wt.% and 12 wt.%) of the biochar produced at 400 °C, 600 °C, 800 °C and 1000 °C and characterized using X-Ray diffraction, scanning electron microscope, Fourier transform infrared spectroscopy. The experimental findings revealed that biochar produced at a higher pyrolyzing temperature could significantly improve the electrical conductance of the biocomposite film. A maximum electrical conductance of 7.67 × 10−2 S was observed for 12 wt.% addition of biochar produced at 1000 °C. A trend of improvement in the electrical properties of the biocomposite films suggested a threshold wt.% of the biochar needed to make a continuous conductive network across the biocomposite film. Rapid degradation of tensile strength was observed with an increasing level of biochar dosage. The lowest tensile strength 3.12 MPa was recorded for the film with 12 wt.% of biochar produced at 800 °C. Pyrolyzing temperature showed a minor impact on the mechanical strength of the biocomposite. The prepared biocomposites could be used as an electrically conductive layer in electronic devices.