Fire Properties of Acrylonitrile Butadiene Styrene Enhanced with Organic Montmorillonite and Exolit Fire Retardant

Abstract

In this paper an experimental investigation on fire retardancy of a new polymer nanocomposite derived from organic montmorillonite and exolit fire retardant in an acrylonitrile- butadiene-styrene copolymer by analyzing the flammability and fire behavior is described. The samples were prepared by melting and mixing nanocomposites and fire retardant in different concentrations in an acrylonitrile-butadiene-styrene base polymer. It was found that using only one component (organic montmorillonite or fire retardant) the burning stops in 10 s on the sample. Confirmation of synergy in flammability by combining both montmorillonite and flame retardants was noticed and is discussed regarding the flame-retardant mechanisms assessed by means of the Limiting oxygen index (LOI), UL 94, and cone-calorimeter methods. The acrylonitrile- butadiene-styrene preparation with 15–20 wt% fire retardant and 1–2 wt% organic montmorillonite reached a UL-94 V-0 classification, contrasting with the pure acrylonitrile- butadiene-styrene and the acrylonitrile-butadiene-styrene with 15 wt% fire retardant and acrylonitrile-butadiene-styrene with 1–2 wt% organic montmorillonite formulations, which completely burned. Finally, the samples showed a very good synergy going to a higher reduction of the peak heat release rate and to a minimum mass reduction, as obtained from cone calorimeter tests.