Effect of Silica Size and Content on Superamphiphobic Properties of Silica-Fluoropolymer Core-Shell Coatings

Author:

Lee JiyoungORCID,Hwang Ha SooORCID,Lo Tien N. H.ORCID,Koh Won-Gun,Park InORCID

Abstract

We present a facile approach to fabricate superamphiphobic surfaces by spray coating silica-fluoropolymer core-shell particles without substrate pretreatment with an additional binder resin. A series of SiO2@poly(1H,1H,2H,2H-heptadecafluorodecyl methacrylate) (SiO2@PFMA) core-shell particles with core particles of different sizes were prepared via thiol-lactam initiated radical polymerization (TLIRP). The surface of each SiO2 particle with an average particle size of 12, 80, 150, and 350 nm was modified with (3-mercaptopropyl) trimethoxysilane and used as a seed for TLIRP. The SiO2@PFMA particles with various SiO2 sizes and contents were coated on aluminum substrates by a spray gun and then thermally treated to form a stable, rough composite layer. During the spray coating, the core-shell particles were aggregated by rapid evaporation of the solvent and then irregularly adhered to the substrate resulting in hierarchical structures. In the case of SiO2@PFMAs with low SiO2 contents, the roughness created mainly by the polymer shell disappeared during heat treatment. However, the substrates coated with SiO2@PFMAs with high SiO2 contents maintained the roughness even after heat treatment. The core-shell particles prepared with 12 nm SiO2 formed a stable superamphiphobic surface. The water/hexadecane contact and sliding angles on an aluminum plate coated with SiO2@PFMA, prepared using 12 nm silica at 46 wt% silica content (12 nm-SiO2(46)@PFMA), were 178.5°/159.2° and 1°/7°, respectively. The cross-cut tape test showed that adhesion between the 12nm-SiO2(46)@PFMA and the aluminum substrate was classified as 5B. A glass surface spray-coated with the core-shell composite particles exhibited transparent superhydrophobicity and translucent superamphiphobicity by controlling the concentration of the coating solution.

Publisher

MDPI AG

Subject

Polymers and Plastics,General Chemistry

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3