Abstract
In this study, Fe-25Mn-9Al-8Ni-1C-xTi alloy (x = 0, 0.1, 0.2, 0.3, 0.4 wt.%) was prepared by vacuum arc melting, and the corresponding microstructure and oxidation behavior at 600 °C were studied. The results show that Fe-25Mn-9Al-8Ni-1C-xTi alloy mainly contains austenite phase, ferrite phase and TiC phase. With Ti content increasing, the austenite phase content decreases, while the contents of ferrite phase and TiC phase increase. The oxidation performance test results show that the addition of Ti element greatly reduces the oxidation weight gain of the alloys at the initial oxidation stage. With the extension of the oxidation time and the further increase of the Ti content, the alloys oxidation weight gain shows a trend of first increasing and then decreasing. When the Ti content is 0.2 wt.%, the oxidation weight gain of this series of alloy reaches the lowest value during the stable oxidation period. Compared with Fe-25Mn-9Al-8Ni-1C alloy, its weight gain per unit area is reduced by 21.1%. Fe-25Mn-9Al-8Ni-1C-xTi alloy oxide layer exhibits a double-layer structure. The outer oxygen layer is mainly loose iron-oxides, while in the inner oxygen layer, the oxides are mainly composed of manganese-oxides and aluminum-oxides, which are relatively dense.
Funder
National Natural Science Foundation of China
Subject
General Materials Science
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献