Shear Bond Strength of Veneered Zirconia Repaired Using Various Methods and Adhesive Systems: A Comparative Study

Abstract

The aim of the present study was to investigate the shear bond strength of five different repair methods and adhesive systems for zirconia (Zr) cores layered with feldspathic porcelain. Seventy-five Zr specimens (10 × 10 × 4 mm3) were prepared, sintered, layered with 2 × 10 × 10 mm3 of feldspathic porcelain, and fired. The ceramic was fractured, and the load recorded using a shear-bond test. Specimens were thermocycled and randomly divided into 5 groups (n = 15/group) based on the repair methods. Composite repair blocks with similar dimensions to the layered ceramic (2 × 10 × 10 mm3) were built according to each repair method. Shear bond strength testing of the specimens with composite built up was carried out using a universal testing machine (Instron®5960, Massachusetts, USA). The shear bond strengths of the adhesive interface between repaired composite and the Zr were recorded for all the test groups. The fractured specimens’ surfaces were examined under a scanning electron microscope (Jeol, Musashino, Akishima, Tokyo, Japan) for evaluation of the type of failure and surface characteristics. Shear bond strength of the veneered ceramic bonded to the Zr for all the test groups was non-significant (ANOVA, p = 0.062). Shear bond strength after the repair revealed significant differences (ANOVA, p = 0.002). Group-C (13.79 ± 1.32) and Group-D (9.77 ± 4.77) showed the highest and lowest shear bond strength values, respectively. Paired Sample T-tests showed significantly lower values (p = 0.000) for the repaired (composite) Zr compared to the layered (ceramic) Zr. Multiple comparisons revealed differences (significant) between the shear bond strength of Group-D with Groups A (p = 0.010) and C (p = 0.003, Post Hoc Tukey test). The repair methods tested showed variations in their respective shear bond strengths. Complete ceramic/zirconia repair systems showed better bonding between the repaired composite and Zr core. The mean shear bond strength for the repaired fractured layered Zr showed acceptable outcomes in terms of clinical perspective, but was, however, unpredictable.