Abstract
Wood-based products usually have serious limitations concerning contact with water, both because wood is a hygroscopic material and because the commonly used binder has low moisture resistance. This paper studies the effect of panel moisture content (MC) on the physico-mechanical properties of medium density fiberboards (MDF). Several commercial MDF boards produced in Europe were stored at room temperature and relative humidity (RH) for 9 weeks (approx. range 15–20 °C and 50–85% RH). Every week, a strip of each MDF board was cut out, divided into 5 × 5 cm test pieces and its internal bond strength (IB) was measured. A strong influence of MDF moisture content on internal bond strength was observed and therefore IB test pieces were stored in a climatic chamber (either at 20 °C, 55% RH and at 20 °C, 70% RH). A decreasing linear relation was established between IB and MC. It was found that this effect is reversible: after drying, internal bond strength rises again (following a slight hysteresis). This work reinforces the importance of conditioned storage before board properties analysis, as described in European Standard EN 319.
Subject
Polymers and Plastics,General Chemistry
Reference30 articles.
1. Fiberboards—Specifications. Part 5. Requirements for Dry Process Boards,2009
2. Urea–formaldehyde (UF) adhesive resins for wood
3. MODELING AND SIMULATION OF THE HOT-PRESSING PROCESS IN THE PRODUCTION OF MEDIUM DENSITY FIBERBOARD (MDF)
4. Transport Phenomena;Carvalho,2010
5. Wood Handbook—Wood as an Engineering Material,2010
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献