Aramid fibre-reinforced epoxy composites (AF/EP) are promising materials in the aerospace, transportation, and civil fields owing to their high strength, high modulus, and light weight. Thick composite laminates are gradually being applied to large composite structures such as wind turbine blades. During curing, temperature overheating is a common problem in thick composites, which leads to matrix degradation, thermal residual stresses, and uneven curing. This paper proposes a signal-to-noise ratio (SNR) method to optimise the curing cycle of thick AF/EP laminates and reduce the overheating temperature. During curing, the temperature and strain evolution in a thick AF/EP laminate were monitored using fibre Bragg grating sensors. The effects of the curing factors on the overheating temperature of the thick AF/EP laminate were evaluated using the Taguchi method and predicted via the SNR method and analysis of variance. The results indicate that the dwelling temperature is the main factor affecting the overheating temperature. The optimal curing cycle involves an overheating temperature of 192.72 °C, which constitutes an error of 2.58% compared to the SNR method predictions. Additionally, in comparison to the initial curing cycle, the overshoot temperature in the optimised curing cycle was reduced by 58.48 °C, representing a reduction ratio of 23.28%.
Funder
the National Key R&D Program of China
Subject
Polymers and Plastics,General Chemistry
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献