Deformation Inhomogeneities of a Hypoeutectic Aluminum-Silicon Alloy Modified by Electron Beam Treatment

Author:

Ustinov Artem1ORCID,Klopotov Anatoly1ORCID,Ivanov Yuri2ORCID,Zagulyaev Dmitry3ORCID,Teresov Anton2ORCID,Petrikova Elizaveta2ORCID,Gurianov Denis4ORCID,Chumaevskii Andrey4ORCID

Affiliation:

1. Faculty of Civil Engineering, Tomsk State University of Architecture and Building, Solyanaya Sq. 2, Tomsk 634003, Russia

2. Institute of High Current Electronics SB RAS, Akademicheskij Ave. 2/3, Tomsk 634055, Russia

3. Department of Natural Sciences Named after Professor V.M. Finkel, Siberian State Industrial University, Kirova Str. 42, Novokuznetsk 654007, Russia

4. Institute of Strength Physics and Materials Science, Siberian Branch of Russian Academy of Sciences, Akademicheskij Ave. 2/4, Tomsk 634055, Russia

Abstract

This paper presents the results of uniaxial tensile tests on specimens of the hypoeutectic aluminum-silicon alloy A319. According to the results, the influence of surface treatment by pulsed electron beam on the mechanical properties of the material was determined. The peculiarities of deformation localization in the material caused by grinding of the surface layer material structure due to rapid crystallization during electron beam treatment were revealed. The surface treatment up to the depth of 100 µm leads to the formation of a fine dendritic columnar structure of silumin and to an increase in the plasticity of the samples. The influence of the surface treatment affects the increase in the deformation localization in the region of the stable concentrator before failure. The greatest increase in ductility and localization of deformation occurs during treatment with an energy density of 15 J/cm2. In the process of specimen deformation, unstable, metastable, and stable areas of plastic deformation localization are formed and replaced, and the formation of stable areas of localized plastic deformation, in which the specimen fails at the end of the test, can be detected at the initial stages of testing. In specimens, during the test in the zone of localized plastic deformation, bands are formed which pass through the entire surface of the specimen at an angle of 35 to 55 degrees to the tensile axis, and their development leads to the formation of stable zones of localized plastic deformation and to the failure of the specimen.

Funder

Ministry of Education and Science of the Russian Federation

Russian Science Foundation

Publisher

MDPI AG

Subject

General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3