Abstract
Coatings were produced on the EP741NP nickel alloy substrates by electrospark deposition (ESD) in argon using an MoSi2-MoB-HfB2 electrode. In situ high-resolution transmission electron microscopy and X-ray diffraction analysis studies have identified the temperature above which the strengthening Mo2Ni3Si Laves phase is formed in the coatings. At 25 °C, the coatings with a predominant content of the Laves phase are characterized by enhanced wear resistance, as well as a lower coefficient of friction compared to the non-annealed coatings containing binary silicides. At 700 °C, the EP741NP substrate was characterized by the lowest friction coefficient (Ktr = 0.35), and its wear was approximately at the same level as the wear of both coatings.
Subject
General Materials Science
Reference31 articles.
1. Assessment of Russian P/M Superalloy EP741NP
2. Sovremennye Zharoprochnye Nikelevye Splavy Dlja Diskov Gazovyh Turbin [Modern Nickel Superalloys for Gas Turbine Discs];Logunov,2013
3. P/M Ni Base Superalloy Encreases Service Life of AL31FP Engines for Sukhoy Fighters;Garibov;Proceedings of the ASM Internationals 13th Advanced Aerospace Materials and Processes Conference and Exposition, The Rosen Plaza,2002
4. Transition metal silicides: fundamentals, preparation and catalytic applications
5. The oxidation behaviour of uniaxial hot pressed MoSi2 in air from 400 to 1400 °C
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献