Effect of Different Types of Block Copolymers on Morphology, Mechanical Properties, and Fracture Mechanisms of Bisphenol-F Based Epoxy System

Abstract

The effect of adding different types of soft block copolymer on the tensile properties, fracture mechanic properties, and thermo-mechanical properties of bisphenol F based epoxy resin were studied. Two different self-assembling block copolymers, (a) constituting of a center block of poly (butyl acrylate) and two side blocks of poly (methyl) methacrylate-co-polar co-monomer (BCP 1) and (b) poly(ethylene oxide)-b-poly(butylene oxide) (PEO-PBO) diblock copolymer (BCP 2), were used with an epoxy-hardener system. The maximum fracture toughness and fracture energy were measured as KIc = 2.75 MPa·m1/2 and GIc = 2.37 kJ/m2 for the 10 wt % of BCP 1 modified system, which were 366% and 2270% higher in comparison to reference epoxy system, and a 63% reduction in tensile strength was also observed. Similarly, for BCP2 modified systems, the maximum value of KIc = 1.65 MPa·m1/2 and GIc = 1.10 kJ/m2 was obtained for epoxy modified with 12 wt % of BCP2 and a reduction of 32% in tensile strength. The fracture toughness and fracture energy were co-related to the plastic zone size for all the modified systems. Finally, the analysis of the fracture surfaces revealed the toughening micro-mechanisms of the nanocomposites.