The idea of flexible body armor has been around for many years. Initial development included shear thickening fluid (STF) as a backbone polymer to impregnate ballistic fibers such as Kevlar. At the core of the ballistic and spike resistance was the instantaneous rise in viscosity of STF during impact. Increase in viscosity was due to the hydroclustering of silica nanoparticles dispersed in polyethylene glycol (PEG) through a centrifuge and evaporation process. When STF composite was dry, hydroclustering was not possible due to absence of any fluidity in PEG. However, particles embedded within the polymer, covered the Kevlar fiber and offered some resistance to spike and ballistic penetration. The resistance was meagre and hence, the goal was to improve it further. This was achieved by creating chemical bonds between particles, and by strongly attaching particles to the fiber. PEG was replaced with silane (3-amino propyl trimethoxysilane), and a fixative cross-linker, Glutaraldehyde (Gluta), was added. Silane installed an amine functional group on the silica nanoparticle surface, and Gluta created strong bridges between distant pairs of amine groups. Amide functional groups present in Kevlar also interacted with Gluta and silane to form a secondary amine, allowing silica particles to attach to fiber. A network of amine bonding was also established across the particle-polymer-fiber system. In synthesizing the armor, silica nanoparticles were dispersed in a mixture of silane, ethanol, water, and Gluta, maintaining an appropriate ratio by weight, and using a sonication technique. Ethanol was used as a dispersion fluid and was evaporated later. Several layers of Kevlar fabric were then soaked with the admixture for about 24 h and dried in an oven. Armor composites were tested in a drop tower according to NIJ115 Standard using spikes. Kinetic energy at impact was calculated and normalized with the aerial density of the armor. NIJ tests revealed that normalized energy for 0-layer penetration increased from 10 J-cm2/g (STF composite) to 220 J-cm2/g for the new armor composite, indicating a 22-fold enhancement. SEM and FTIR studies confirmed that this high resistance to spike penetration was due to the formation of stronger C-N, C-H, and C=C-H stretches facilitated by the presence of silane and Gluta.
Subject
Inorganic Chemistry,Organic Chemistry,Physical and Theoretical Chemistry,Computer Science Applications,Spectroscopy,Molecular Biology,General Medicine,Catalysis
Reference20 articles.
1. Egres, R.G., Lee, Y., Kirkwood, J., Wagner, N., and Wetzel, E. (2003, January 14–18). Novel flexible body armor utilizing shear thickening fluid (STF) composites. Proceedings of the 14th International Conference on Composite Materials, San Diego, CA, USA.
2. Dynamic properties of shear thickening colloidal suspension, Rheo;Lee;Acta,2003
3. Soft armor materials constructed with Kevlar fabric and a novel shear thickening fluid;Qin;Compos. Part B,2020
4. Effect of Particle Hardness on the Penetration Behavior of Fabrics Intercalated with Dry Particles and Concentrated Particle−Fluid Suspensions;Kalman;ACS Appl. Mater. Interfaces,2009
5. Optimal designing of soft body armor materials using shear thickening fluid;Majumdar;Mater. Des.,2013
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献