Effect of Rolling Temperature on the Microstructure and Mechanical Properties of Mg-2Zn-0.4Y Alloy Subjected to Large Strain Rolling

Author:

Wang Tong,Zhou Xiong,Li Yafang,Zhang Zhiqiang,Le Qichi

Abstract

Large strain rolling (LSR) has been conducted on the Mg-2Zn-0.4Y alloy. After the 1st rolling process at 250, 300, 350, and 400 °C, the alloy demonstrates a fully recrystallized microstructure. The grain size increases from 6, 8, 12, to 17 μm with an increasing rolling temperature. After the 2nd rolling process at 300 °C, twinning and shear bands were introduced. During the 3rd rolling process at 350 °C, dynamic recrystallization (DRX) was observed and resulted in a more uniform microstructure. DRX occurred because of temperature increase and large dislocation density induced by LSR. For the room temperature tensile tests, the plates rolled at 300 and 350 °C in the 1st rolling process demonstrate higher strength and lower elongation due to twinning. The one rolled at 400 °C in the 1st rolling process, shows the most uniform rolling microstructure and the best combination of strength and elongation at room temperature.

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3