Preparation of High Hardness Transparent Coating with Controllable Refractive Index by Sol-Gel Technology

Abstract

SiO2/ZrO2 and SiO2/ZrO2/Al2O3 composite organic–inorganic coatings were prepared by the sol-gel technology. The structure of the coating was characterized by IR, particle size analyzer, SEM, and AFM, respectively. The results showed that ZrO2, SiO2 (inorganic component), and siloxane had undergone a hydrolytic condensation reaction, and the composite organic–inorganic coatings were formed with -O-M-O- (M is Si, Zr) as molecular skeleton network structure. Adding an appropriate ratio of ZrO2 sol, no agglomeration and phase separation occurred, which could significantly improve the refractive index, hardness, and light transmittance of the coatings. Al2O3 sol could greatly improve the friction resistance of the composite organic–inorganic coatings, and the Bayer ratio of the composite coatings could reach 7.86. By adjusting the proportioning of composite sol solution, the refractive index of the composite transparent coatings could be controlled from 1.52 to 1.65.