An Experimental Study for the Improvement of the Stain Resistance for Exterior Wall Paints in a Western City in China

Abstract

In recent years, with the rapid development of the building industry in western cities during the period of “Western Development” in China, the paints industry has developed rapidly and become more mature. In addition, waterborne inorganic exterior wall paints have been a great choice in the building industry because of their reduced volatile organic compounds (VOCs) and less toxicity and odor. However, the problem of stain resistance for exterior wall paints in western cities has not been solved, which has become a major obstacle to the application and promotion of exterior wall paints in western cities in China. Therefore, effective measures should eventually be carried out for improving the stain resistance of exterior wall paints in western cities in China. In this paper, an experimental study on improving stain resistance for exterior wall paints in a typical western city in China, Chongqing, is reported. In the three defined designs, the effects of the paint structure type, the pigment volume concentration (PVC), thickeners, cosolvents and wetting and dispersing agents on the stain resistance of exterior wall paints in a typical western city in China, Chongqing, were examined. The experimental results suggest that the stain resistance of silicone–acrylic paint was the most suitable among the three kinds of tested paints (silicone–acrylic paint, styrene–acrylic paint and pure acrylic paint). In addition, the PVC had a great influence on the stain resistance of the exterior wall paints. The compactness, water absorption and stain resistance of the paint’s film were the most suitable when the PVCs of the paints reached 45%. Furthermore, the tested wetting and dispersing agents made the same contributions to the paints’ stain resistance, as their decline rates for reflectivity were similar. The reflectivity of the film significantly decreased when the ratio of associating thickener to non-associating thickener reached 4:1, and also significantly declined when the content of propylene glycol reached 5%.