Solid-to-Liquid Ratio Influenced on Adhesion Strength of Metakaolin Geopolymer Coating Paste Added Photocatalyst Materials

Abstract

Coating materials are used on surfaces such as steel and ceramic to offer protection, corrosion resistance, wear and erosion resistance, a thermal barrier, or aesthetics. Although organic coating materials such as epoxy resins, silane, and acrylic are widely used, there are restrictions and drawbacks associated with their use, including the ease with which cracking, hazardous and harmful human health and environment, peeling, and deterioration occur. Organic matrices also have the capacity to release vapor pressure, which can lead to the delamination of coatings. Geopolymer coating materials offer an environmentally friendly solution to this concern to encourage sustainable growth. The simplicity with which geopolymers can be synthesized and their low emission of greenhouse gases such as CO2, SO2, and NOx are advantages of geopolymers. The advent of geopolymer coatings with photocatalytic properties is advantageous for the decomposition of pollution and self-cleaning properties. The aim of this paper is to study the optimum solid-to-liquid ratio of metakaolin geopolymer paste added TiO2 and ZnO by adhesion strength. Through iterative mixture optimization, we investigated the effects of different design parameters on the performance of a metakaolin-based geopolymer as a coating material. The assessed material was a metakaolin which was activated by an alkali activator (a mixture of sodium hydroxide and sodium silicate), with the addition of titanium dioxide and zinc oxide as photocatalyst substances. Varying proportions of solid-to-liquid ratio were tested to optimize the best mix proportion related to the coating application. Adhesion analyses of geopolymer coating paste were evaluated after 7 days. According to the findings, the optimal parameters for metakaolin geopolymer coating material are 0.6 solid-to-liquid ratios with the highest adhesion strength (19 MPa) that is suitable as coating material and enhanced the properties of geopolymer.