Preparation and Properties of High Hardness Ultraviolet Curable Polyethylene Terephthalates Surface Coatings Modified with Octavinyl-Polyhedral Oligomeric Silsesquioxane

Abstract

Using organic coatings helps to protect PET (polyethylene terephthalates) surfaces, improve surface hardness, scratch resistance, and solvent resistance, prolong the service life of PET film, and to expand their scope of applications. There were some disadvantages, including poor flexibility and impact resistance in high-hardness coatings; organic coatings should also be modified to improve the toughness. Herein, a UV (ultraviolet curing) curable high-hardness organic coating used in PET surface protection was prepared and modified with inorganic nanoparticles, such as OVPOSS (octavinyl-polyhedral oligomeric silsesquioxane). The effects of the categories of nanoparticles on the coating performance were studied. UV-Vis spectra (ultraviolet visible light spectra), FT-IR (Fourier transform infrared spectrometer), TGA (thermogravimetric analysis), DMA (dynamic-mechanical), SEM (field emission scanning electron microscope), and AFM (atomic force microscope) were used to characterize the properties of the coatings. The results showed that the addition of eight-vinyl POSS to the organic coating significantly increased its glass transition temperature (Tg) from 100 to 120 °C, improved its storage modulus from 167.6 MPa to 258.9 MPa, and raised its impact resistance and flexibility. The SEM and AFM images displayed that the eight-vinyl POSS particles were dispersed homogeneously in the coating, arranged in an ordered network, and had good compatibility with organic components. The film displayed excellent properties, including 4 H of the pencil hardness, 100 g cm of impact resistance, excellent flexibility, and 90% of light transmittance, with the addition of 0.3 wt % OVPOSS. TGA analysis revealed that the coating had good thermal stability, with 5% weight loss temperature up to 335 °C.